Harris 5620F1 Stay-Silv 5 Brazing Filler Metal, 1/2 x 1/8 in Dia x 28 in L, #28 Stick
Stay-Silv 5 is used primarily where fit-up cannot be tightly controlled. Stay-Silv 5 is a medium melting range alloy.
Part #31276
Harris 5620F1 Stay-Silv 5 Brazing Filler Metal, 1/2 x 1/8 in Dia x 28 in L, #28 Stick
Stay-Silv 5 is used primarily where fit-up cannot be tightly controlled. Stay-Silv 5 is a medium melting range alloy.
Part #31276
- Stay-Silv 5 silver brazing filler metal designed for copper-to-copper applications
- Also used on copper-to-low zinc by applying Stay-Silv white brazing flux
- Stay-Silv 5 will flow rapidly when heated quickly to its liquidus, this allows penetration into tight clearance connections, with slower heating the alloy melting range provides ability to fill wider gaps
- Economical alternative to higher silver content alloys for copper and brass applications
- Not recommended for brazing steel or other ferrous base metals, as the phosphorus content promotes formation of low ductility intermetallic with the base metal
- Corrosion resistance is generally similar to copper base metal, but phosphorus containing alloys, including Stay-Silv 5, should not be used if the braze is exposed to sulfur or sulfur compounds in service
- Medium range alloy is well suited where close fit-up cannot be maintained
- Filler metal is somewhat more ductile than Harris or Stay-Silv 2
- AWS A5.8 BCuP-3|ASME SFA 5.8 BCuP-3|PROP65: Cancer and Reproductive Harm - www.P65Warnings.ca.gov|RoHS Compliant
- Brand:Â HarrisApplicable Materials:Â Copper/Brass, Copper to CopperBrazing Range:Â 1350 to 1550 deg FChemical Composition:Â 5.9% Phosphorus, 5% Silver, Copper Balance and 0.15% OtherContainer Size:Â #28Container Type:Â StickCountry of Origin:Â USDiameter:Â 1/2 x 1/8 inLength:Â 28 inManufacturer Name:Â Harris Products GroupSeries:Â Stay-Silv 5