Harris 0620F1 Brazing Filler Metal, 1/2 x 1/8 in Dia x 28 in L, #28 Stick
Harris low cost alloy for many copper to copper applications where moderate fit-up can be maintained and brazing temperature is Not critical.
Part #32907
Harris 0620F1 Brazing Filler Metal, 1/2 x 1/8 in Dia x 28 in L, #28 Stick
Harris low cost alloy for many copper to copper applications where moderate fit-up can be maintained and brazing temperature is Not critical.
Part #32907
- Harris Low cost alloy suitable for most copper-to-copper or brass joints where good fit-up exists and assemblies are not subject to excessive vibration nor movement
- This alloy flows quickly at brazing temperature so requires close joint tolerance, less than 0005 in is a frequent choice for copper brazing
- A suitable choice for brazing brass, operators should take care to avoid over heating the brass and use Harris Stay-Silv white brazing flux in this application
- Not recommended for brazing steel or other ferrous base metals, the phosphorus content will form a low ductility intermetallic with the base metal
- Corrosion resistance is generally similar to copper base metal, but phosphorus containing alloys, including Harris , should not be used if the braze is exposed to sulfur or sulfur compounds in service
- AWS A5.8 BCuP-2|ASME Section IIC SFA 5.8 BCuP-2|ISO 17672 CuP 181|PROP65: Cancer and Reproductive Harm - www.P65Warnings.ca.gov|RoHS Compliant
- Brand:Â HarrisApplicable Materials:Â Copper to Copper and Copper to brassBrazing Range:Â 1345 to 1500 deg FChemical Composition:Â 7.1% Phosphorus, Copper Balance and 0.15% OtherContainer Size:Â #28Container Type:Â StickCountry of Origin:Â USDiameter:Â 1/2 x 1/8 inLength:Â 28 inManufacturer Name:Â Harris Products Group